Composition and performance:
Two-component electrostatic conductive primer made of epoxy resin, conductive additive, non-carbon conductive filler, chemical anti-rust pigment, polyamide resin, etc.
Excellent adhesion and anti-seepage performance
Good long-term conductivity
Excellent acid, alkali, salt and oil resistance
Excellent sealing performance
use:
Applicable to the inner wall of various oil storage tanks and transportation equipment with static electricity conduction requirements for anti-corrosion and anti-rust
Technical indicators:
project | Performance Indicators | |
color | Gray, iron red | |
Status in the container | After stirring and mixing, there is no hard lump and it is in a uniform state | |
Construction | Barrier-free application | |
Coating appearance | Smooth | |
Gloss (60°)/°, ≥ | 30 | |
Fineness/μm, ≤ | 50 | |
Drying time/h, ≤ | Touch Dry | 1.5 24 |
Get down to business | ||
Non-volatile matter/%,≥ | 60 | |
Impact resistance/cm | 50 | |
Bending test/mm | 1 | |
Surface resistance | 10 5 -10 9 Ω | |
Moisture and heat resistance (1000h), grade | 1 | |
Salt spray resistance, 720h | Level 1 , coating without red rust | |
Gasoline resistance (60℃, 720h) | The paint film is intact, without peeling, wrinkling, blistering, cracking, rusting, discoloration, etc., and the gloss loss rate is ≤20% | |
Alkali resistance (5% NaOH solution) | The paint film is intact, without peeling, wrinkling, blistering, cracking, rusting, discoloration, etc., and the gloss loss rate is ≤20% | |
Acid resistance (5% H 2 SO 4 solution) | The paint film is intact, without peeling, wrinkling, blistering, cracking, rusting, discoloration, etc., and the gloss loss rate is ≤20% | |
Construction instructions:
Main agent: curing agent = 10: 1, stir evenly, add 10-15% epoxy diluent, and apply by high-pressure airless spray, brush or roller.
Surface treatment:
The steel surface treatment is carried out in accordance with the national standard "Surface rust grade and rust removal grade of steel before painting" GB8923-88. Sandblasting rust removal reaches the national standard Sa2.5 grade, and manual rust removal reaches St3 grade.
Notes:
1. The paint should be stored in a low temperature, ventilated and dry place; away from fire and heat sources; the shelf life is one year in a cool and dry place.
2. The above information is written based on actual testing and usage experience of our company's technical personnel and can be used as a construction guide. However, due to differences in coating environments and supporting solutions, it is recommended that users conduct preliminary experiments and tests based on actual needs and uses before confirming use. Our company only guarantees the quality and stability of this product itself.
If you have any questions, please contact us promptly and we will answer your questions as soon as possible.