Composition and performance:
Component A base material:
Resins, pigments and fillers, special additives, etc.
Component B base material:
Curing agent.
When component A and component B are mixed in equal amounts, the three networks interpenetrate at the molecular level to form an interpenetrating polymer network (IPN) structure, producing a synergistic effect. The coating network has the following characteristics: strong adhesion, good flexibility, and resistance to corrosive media such as acids, alkalis, and salts. The coating's toughness, strength, adhesion, permeability resistance, and chemical inertness are further improved, giving the coating film better performance. Improving the performance of polymers by forming IPN is a new type of polymer blending technology. The paint film has good rust resistance and acid resistance.
The paint film has good oil resistance, water resistance and wear resistance
The paint film dries quickly and has strong adhesion
The paint film has excellent matching
use:
It is suitable for the anti-corrosion of steel structure surfaces, non-metallic surfaces, bridges, water tanks, gas tanks, oil tanks, buried pipelines, electricity, oil tanks, metallurgy, chemical industry and civil use. It is suitable for the anti-corrosion of ships and steel structures in chemical atmosphere and marine atmosphere. It is suitable for coating the surface of galvanized steel plates with appropriate roughening treatment.
Technical indicators:
project | Performance Indicators | |
color | Iron red, gray | |
Status in the container | After stirring and mixing, there is no hard lump and it is in a uniform state | |
Construction | Trouble-free application | |
Coating appearance | Smooth | |
Gloss (60°)/°, ≥ | 25 | |
Fineness/μm, ≤ | 50 | |
Drying time/h, ≤ | Touch Dry | 1 twenty four |
Get down to business | ||
Non-volatile matter/%,≥ | 70 | |
Impact resistance/cm | 50 | |
Bending test/mm | 1 | |
Cross-cut test/level | 1 | |
Salt water resistance (3% NaCl solution, 720h ) | No abnormality | |
Water resistance (720h) | No bubbling, no shedding, slight discoloration allowed | |
Alkali resistance (5% NaOH solution, 72h) | No abnormality | |
Acid resistance (5% H 2 SO 4 solution, 72h) | No abnormality | |
Gasoline resistance (48h) | No foaming, no softening, no stickiness | |
Construction instructions:
Main agent: curing agent = 10:1, stir evenly, add 10-15% of IPN supporting diluent, and apply by high-pressure airless spray, brush or roller.
Surface treatment:
The steel surface treatment is carried out in accordance with the national standard "Surface rust grade and rust removal grade of steel before painting" GB8923-88. Sandblasting rust removal reaches the national standard Sa2.5 grade, and manual rust removal reaches St3 grade.
Notes:
1. The paint should be stored in a low temperature, ventilated and dry place; away from fire and heat sources; the shelf life is one year in a cool and dry place.
2. The above information is written based on actual testing and usage experience of our company's technical personnel and can be used as a construction guide. However, due to differences in coating environments and supporting solutions, it is recommended that users conduct preliminary experiments and tests based on actual needs and uses before confirming use. Our company only guarantees the quality and stability of this product itself.
If you have any questions, please contact us promptly and we will answer your questions as soon as possible.